CoTMPP/MWNT electrocatalys shows 10 mV higher on-set potential for oxygen reduction and 21% lower reduction current loss in comparison to CoTMPP/BP2000. That means that multiwalled carbon nanotube supported CoTMPP electrocatalyst has higher catalytic activity and better stability than CoTMPP/BP2000.
结果表明,与有机回流合成法制备的催化剂相比,微波法合成的CoTMPP/MWNT具有更好的氧还原性能,半波电位正向移动110 mV;与多孔碳负载的CoTMPP/BP2000比较,多壁碳纳米管作为载体的CoTMPP/MWNT电催化剂的起始电位高10 mV,还原电流损失低21%,表现出更好的氧还原活性和稳定性。